Fabrication of Exchange-Coupled α-Fe/Nd-Fe-B Multilayer Thin-Film Magnets
نویسندگان
چکیده
منابع مشابه
Properties of Exchange Coupled All-garnet Magneto-Optic Thin Film Multilayer Structures
The effects of exchange coupling on magnetic switching properties of all-garnet multilayer thin film structures are investigated. All-garnet structures are fabricated by sandwiching a magneto-soft material of composition type Bi1.8Lu1.2Fe3.6Al1.4O12 or Bi₃Fe₅O12:Dy₂O₃ in between two magneto-hard garnet material layers of composition type Bi₂Dy₁Fe₄Ga₁O12 or Bi₂Dy₁Fe₄Ga₁O12:Bi₂O₃. The fabricated ...
متن کاملMagnetic properties of Nd-Fe-B/α-Fe multi-layered thick film magnets
Nd-Fe-B/α-Fe multi-layered nanocomposite film-magnets were prepared from a rotating Nd2.6Fe14B/α-Fe composite target by the pulse laser deposition method with a NdYAG laser (λ=355 nm). The prepared film-magnets were composed of approximately 800 layers with the thickness of about several tens nanometre, and exhibited hard magnetic properties after annealing. The laser power for the ablation of ...
متن کاملDesign and fabrication of multilayer thin film coated hollow waveguides for enhanced infrared radiation delivery
Metal coated Hollow Glass Waveguides (HGWs) incorporating single dielectric thin films have been widely used for the low-loss transmission of infrared radiation in applications ranging from surgery to spectroscopy. While the incorporation of single dielectric film designs have traditionally been used in metal/dielectric coated HGWs, recent research has focused on the development of alternating ...
متن کاملExplosive shock processing of Pr2Fe14B/ –Fe exchange-coupled nanocomposite bulk magnets
Explosive shock compaction was used to consolidate powders obtained from melt-spun Pr2Fe14B/ –Fe nanocomposite ribbons, to produce fully dense cylindrical compacts of 17–41-mm diameter and 120-mm length. Characterization of the compacts revealed refinement of the nanocomposite structure, with approximately 15 nm uniformly sized grains. The compact produced at a shock pressure of approximately 1...
متن کاملExchange-coupled nanoscale SmCo/NdFeB hybrid magnets
Nanoscale hybrid magnets containing SmCo5 and Nd2Fe14B hard magnetic phases have been produced via a novel ‘‘in-one-pot’’ processing route. The grain size of the processed bulk composite materials is controlled below 20 nm. The refinement of the nanoscale morphology leads to effective inter-phase exchange coupling that results in single-phase like magnetic properties. Energy product of 14 MGOe ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1998
ISSN: 0285-0192,1880-4004
DOI: 10.3379/jmsjmag.22.s1_346