Fabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition

Fabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition

Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morph...

Fabrication of nanowires and nanotubes by anodic alumina template-assisted electrodeposition

Fabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores

A simple method for fabrication of highly ordered gold nanorod film is introduced in this article. The procedure is based on thermal evaporation of gold into a porous anodic alumina film (PAA). The PPA film was fabricated by combining the hard and mild anodization. This combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with c...

Electrochemical fabrication of Cu/Pd multilayer nanowires in polycarbonate template

  In this work,copper/palladium (Cu/Pd) multilayer nanowires were successfully prepared by electrodeposition method using polycarbonate template. The fabrication of Pd/Cu multilayer nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The morphological properties of the nanowires were studied by scanning electron microscopy (SEM) and resu...

fabrication of highly ordered gold nanorods film using alumina nanopores

a simple method for fabrication of highly ordered gold nanorod film is introduced in this article. the procedure is based on thermal evaporation of gold into a porous anodic alumina film (paa). the ppa film was fabricated by combining the hard and mild anodization. this combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with control...