Fabrication of Amorphous Fe-B Alloy Films by Contact Plating Method and Their Magnetic Properties.
نویسندگان
چکیده
منابع مشابه
architecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولFabrication and Magnetic Properties of Amorphous Co1-xPx Alloy Nanowire Arrays
Amorphous Co1-xPx alloy nanowire arrays with different sizes and 6.8 wt% x 9.9 wt% were fabricated in an anodic aluminum oxide film by electrodeposition. Transmission electron microscopy, selected area electron diffraction, X-ray fluorescence spectrometer, inductively coupled plasma-atomic emission spectrometer, X-ray diffraction spectrometer and vibrating sample magnetometer are employed to st...
متن کاملMagnetic properties of amorphous Ni60Ag40 films
Amorphous Ni–Ag films were obtained on liquid nitrogen cooled Si substrates using DC magnetron sputtering. A series of magnetic and magneto-transport property measurements confirm that the film with Ni to Ag atomic ratio of 60:40 is an alloy of the two elements immiscible in equilibrium, with atomic-level intermixing. The magnetic properties of the new alloy are discussed in comparison with tho...
متن کاملStructure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...
متن کاملEffect of Cu Addition on Soft Magnetic Properties of Fe–Zr–Si Amorphous Alloy
The effect of Cu addition on the soft magnetic properties of FeZrSi amorphous alloy was investigated by X-ray analysis, TEM observation, and B-H curve tracer. As a melt-spun amorphous ribbon sample was annealed above the crystallization onset temperature, very fine ¡-Fe particles smaller than 315 nm were precipitated and uniformly distributed in an amorphous matrix. Cu addition to FeZrSi am...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1998
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.49.769