Fabrication and Magnetic Properties of A New Fe-based Amorphous Compound Powder Cores
نویسندگان
چکیده
منابع مشابه
A Comparative Study of Insulators on Magnetic Properties of Sendust Based Nanocomposite Powder Cores
In this study, Sendust (Fe85Si9.6Al5.4) nanostructure alloy was prepared bymechanical alloying and was characterized by X-ray diffraction. In addition, the alloy’smorphology and its distribution particle size were investigated by scanning electronmicroscopy method. The alloyed powders were insulated with 4wt% of three differentinsulating materials including polyvinyl alc...
متن کاملFabrication of Soft Magnetic Fe-based Nanoalloy
The Fe-Ni-Sb-B amorphous alloy has been prepared by a solid-solid chemical reaction of ferric trichloride, nickel chloride, antimony chloride and potassium borohydride powders at room temperature. The inductive couple plasma study indicates that the resultant is composed of Fe 5.38 %, Ni 56.19 %, Sb 29.02 % and B 0.44 %. The XRD and thermal analysis show that the alloy is a non-strict sense amo...
متن کاملEffect of Ribbon Width on the Magnetic Properties of Fe- based Amorphous Cores
The effects of different ribbon widths on the magnetic properties of an amorphous alloy were studied. DSC, TGA, XRD, VSM, SEM and ER techniques were used. For SA1 alloy, the sample during primary crystallization for the 142mm and 213mm width ribbons are quite similar; however the magnetic properties and morphologies are significantly different. Finally, the measurements of a three-phase 2MVA am...
متن کاملfabrication of new ion sensitive field effect transistors (isfet) based on modification of junction-fet for analysis of hydronium, potassium and hydrazinium ions
a novel and ultra low cost isfet electrode and measurement system was designed for isfet application and detection of hydronium, hydrazinium and potassium ions. also, a measuring setup containing appropriate circuits, suitable analyzer (advantech board), de noise reduction elements, cooling system and pc was used for controlling the isfet electrode and various characteristic measurements. the t...
Fabrication and magnetic properties of Fe–Pd nanowire arrays
Ordered 20 nm Fe–Pd nanowire arrays with different compositions have been fabricated by alternating current electrodeposition into nanoporous anodic alumina. The structural and magnetic properties of the arrays were investigated by transmission electron microscopy (TEM), X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). When Fe content is lower than 46 at.%, Fe–Pd alloy phase wit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Magnetics
سال: 2011
ISSN: 1226-1750
DOI: 10.4283/jmag.2011.16.3.318