Fabrication and characterization of Manganese–Zinc Ferrite nanoparticles produced utilizing heat treatment technique
نویسندگان
چکیده
منابع مشابه
Synthesis and Characterization of Nickel Zinc Ferrite Nanoparticles
In this research nickel zinc ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °C for 5 hours. The structure of nanoparticles was studied using X-ray diffraction pattern. The lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticl...
متن کاملFabrication of Mn-ferrite nanoparticles from MnO colloids.
The reaction mechanism for conversion of MnO nanoparticles to Mn-ferrite nanoparticles was studied, which involved sequential consumption of MnO and the growth of ferrite. The method could be applied to other ferrite nanoparticles including cobalt ferrite.
متن کاملsynthesis and characterization of nickel zinc ferrite nanoparticles
in this research nickel zinc ferrite nanoparticles with composition of ni1-xznxfe2o4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °c for 5 hours. the structure of nanoparticles was studied using x-ray diffraction pattern. the lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticles depend on zinc concentration. the crystal...
متن کاملCharacterization of ferrite nanoparticles for preparation of biocomposites
Ferrite nanoparticles with nominal composition Me0.5Fe2.5O4 (Me = Co, Fe, Ni or Mn) have been successfully prepared by the wet chemical method. The obtained particles have a mean diameter of 11-16 ± 2 nm and were modified to improve their magnetic properties and chemical activity. The surface of the pristine nanoparticles was functionalized afterwards with -COOH and -NH2 groups to obtain a bioa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Results in Physics
سال: 2019
ISSN: 2211-3797
DOI: 10.1016/j.rinp.2019.02.019