Extremely rapid age hardening behavior in solution treated Ti-5Al-2Fe-3Mo
نویسندگان
چکیده
منابع مشابه
The Microstructure, Creep, and Tensile Behavior for Ti-5Al-45Nb (Atomic Percent) Fully-b Alloy
The microstructure, tensile, and creep behavior of a Ti-5Al-45Nb (at. pct) alloy was evaluated. The main objective of processing and characterizing this alloy was to obtain the constituent properties of a fully-b Ti-Al-Nb alloy to aid in modeling the tensile and creep properties of twophase orthorhombic + body-centered-cubic (O + bcc) alloys. A second objective was to compare the tensile and cr...
متن کاملSintering Properties of Mechanically Alloyed Ti-5Al-2.5Fe
In this study, Ti-5Al-2.5Fe alloy was prepared by powder metallurgy. The elemental titanium, aluminum, and iron powders were mechanically alloyed for 10 h in a vacuum atmosphere. A stainless steel jar and stainless steel balls were used for mechanical alloying. The alloyed powders were then sintered by vacuum hot pressing at 950 °C for a soaking time of 30 minutes. Pure titanium was also sinter...
متن کاملMagnetic hardening of Zr2Co11:(Ti, Si) nanomaterials
The role of Ti and Si additions in the magnetic hardening of rapidly quenched Zr2Co11-based nanomaterials has been investigated. Nanocrystalline Zr17–xTixCo83 and Zr18Co82–ySiy are mainly composed of rhombohedral Zr2Co11 and a small amount of orthorhombic Zr2Co11, hcp Co, and cubic Zr6Co23. Ti addition decreases the mean grain size of the magnetic phases, and thus increases coercivity and energ...
متن کاملAge Hardening of Ultrafine Grained Al-Ti-Cr Alloys Fabricated by Continuous Electron Beam Evaporation
Supersaturated Al-Ti-Cr alloys were produced by a continuous electron beam evaporation technique. The as-deposited alloy sheets were fcc supersaturated solid solution with an average grain size of about 400 nm. Due to the fine grain size, the hardness of the alloy was as high as 270Hv. The sheet showed age hardening, and the peak hardness of 340Hv was obtained after aging at 623K for 900 s, in ...
متن کاملDynamic Shear Deformation and Failure of Ti-6Al-4V and Ti-5Al-5Mo-5V-1Cr-1Fe Alloys
To study the dynamic shear deformation and failure properties of Ti-6Al-4V (Ti-64) alloy and Ti-5Al-5Mo-5V-1Cr-1Fe (Ti-55511) alloy, a series of forced shear tests on flat hat shaped (FHS) specimens for the two investigated materials was performed using a split Hopkinson pressure bar setup. The evolution of shear deformation was monitored by an ultra-high-speed camera (Kirana-05M). Localized sh...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2020
ISSN: 2261-236X
DOI: 10.1051/matecconf/202032111016