Experimental Determination Of Chloride Penetration In Cracked Concrete Beams
نویسندگان
چکیده
منابع مشابه
Modeling Chloride Penetration in Saturated Concrete
A mathematical model is established for chloride penetration in saturated concrete. The model takes into account various influential parameters such as water-to-cement ratio, curing time, types of cement, and aggregate content. Two material models are developed for binding capacity and chloride diffusivity, which have a dominant effect on the chloride diffusion process. The chloride binding cap...
متن کاملAutogeneous healing and chloride ingress in cracked concrete
An experimental study of the influence of autogeneous healing on chloride ingress in cracked concrete is presented. In the study, two concrete mixtures (a Portland cement mix and a blast furnace slag mix), two healing regimes (submerged and fog room regime), two cracking ages (14 and 28 days), and multiple crack widths are used as parameters. An adapted Rapid Chloride Migration testing procedur...
متن کاملResearch on Chloride Penetration Resistance of Phosphoaluminate Cement Concrete
The chloride penetration resistance of phosphoaluminate cement (PAC) concrete was investigated in this study. The effects of mixture proportioning parameters, including cement content, water–cement ratio (w/c), and superplasticizer content on chloride ion penetration resistance of PAC concrete were investigated by the rapid chloride migration test (RCM). The result shows that the increase of ce...
متن کاملPermeability Study of Cracked Concrete
Cracks in concrete generally interconnect flow paths and increase concrete permeability. The increase in concrete permeability due to the progression of cracks allows more water or aggressive chemical ions to penetrate into the concrete, facilitating deterioration. The present work studies the relationship between crack characteristics and concrete permeability. In this study, feedback controll...
متن کاملMesoscale Modelling of the Chloride Diffusion in Cracks and Cracked Concrete
In service, cracks or microcracks are usually present in concrete as a result of several mechanisms, for example the drying shrinkage, thermal gradients, freezing-thawing cycles, alkali-aggregate reaction and external loading. It has been realized that cracking can significantly accelerate the ingress of chlorides into concrete since it provides preferential flow channels and allow more chlorid...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2011
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2011.11.2661