Exchange bias in [Co2MnGe/Au]n, [Co2MnGe/Cr]n and [Co2MnGe/Cu2MnAl]n multilayers
نویسندگان
چکیده
منابع مشابه
Perpendicular exchange bias and magnetic anisotropy in CoOÕpermalloy multilayers
S. M. Zhou, L. Sun, P. C. Searson, and C. L. Chien Department of Physics and Astronomy, Johns Hopkins University, Baltimore, Maryland 21218, USA Surface Physics Laboratory (State Key Laboratory) and Department of Physics, Fudan University, Shanghai 200433, China Department of Materials Science and Engineering, Johns Hopkins University, Baltimore, Maryland 21218, USA ~Received 18 August 2003; pu...
متن کاملCoercivity and exchange bias of ferromagnetic/antiferromagnetic multilayers
For a model system consisting of a ferromagnetic layer exchange coupled to an antiferromagnetic layer with a compensated interface, detailed mean-field-type calculations are performed. Both the coercive field and the exchange bias field are calculated. For the coercive field, a rather broad enhancement around the Néel temperature TN of the antiferromagnetic layer is found irrespective of whethe...
متن کاملExchange bias in thin-film (Co/Pt)3/Cr2O3 multilayers
We have fabricated exchange-biased Co/Pt layers ((0.3 nm/1.5 nm) 3) on (0 01)-oriented Cr2O3 thin films. The multilayered films showed extremely smooth surfaces and interfaces with root mean square roughness of E0.3 nm for 10mm 10mm area. The Cr2O3 films display sufficient insulation with a relative low leakage current (1.17 10 A/cm at 380MV/m) at room temperature which allowed us to apply elec...
متن کاملExchange Coupling in Magnetic Multilayers
In magnetic multilayers, the magnetizations of two ferromagnetic layers separated by a non-magnetic spacer layer are coupled by the electrons in the spacer layer. This coupling oscillates in sign as a function of the thickness of the spacer layer. Extensive research done on these systems has led to a simple model for this coupling and remarkable agreement between predictions of the model and me...
متن کاملOscillatory exchange coupling in Fe/Cr multilayers.
First-principles calculations of the reflection probabilities for Fermi surface electrons at Cr/Fe interfaces are used to compute the strength of the oscillatory exchange coupling in Cr/Fe multilayers. These calculations show that critical spanning vectors across the N -centered ellipsoids of the Cr Fermi surface cause the long period coupling for (001), (110), and (211) interfaces. The periods...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Magnetism and Magnetic Materials
سال: 2003
ISSN: 0304-8853
DOI: 10.1016/s0304-8853(02)01175-7