Evaluation of thermal shock resistance in ceramic materials.
نویسندگان
چکیده
منابع مشابه
Thermal shock resistance of core reinforced all-ceramic crown systems.
The coefficient of thermal expansion of core and veneer porcelains for all ceramic crowns must be compatible to prevent formation of stresses during the firing cycles. The purpose of this study was to use a thermal shock test to evaluate the crazing resistance of six all-ceramic crown systems. The systems tested were: Vita In-Ceram, Vita Hi-Ceram, Dicor veneered with Vitadur N, magnesia core ve...
متن کاملFactors Affecting Thermal Stress Resistance of Ceramic Materials
ing from temperature gradients in a cylinder were derived by Duhamel (1838).‘ Since that time, about thirty papers have appeared which mainly consider the calculation of thermal stresses in an infinite cylinder subjected to temperature gradients. It is apparent that thermal stresses are not a new or uninvestigated phenomenon. The first quantitative treatment of thermal stress fracture in cerami...
متن کاملThermal shock and thermal fatigue study of ceramic materials on a newly developed ascending thermal shock test equipment
A test equipment was designed to study thermal shock and thermal fatigue of ceramic materials subjected to fast heating (ascending). The equipment was designed to generate thermal stress in a test specimen by heating one surface of it by an oxy-hydrogen flame while cooling the opposite surface. The sample cracked when thermal stress exceeded its mechanical strength. The in situ crack formation ...
متن کاملEvaluation of contemporary ceramic materials.
The last 25 years have witnessed the introduction of a bewildering number of ceramic systems to the dental profession. Most of these systems have been introduced with little or no clinical testing. Laboratory studies of physical and mechanical properties of ceramics provide little predictive information regarding likely clinical survival rates. Early adopters of many of these new systems learne...
متن کاملThermal Stress Resistance to Fracture and its Relation to with Resistance to Thermal Fatigue and Shock
Dense Silicon nitride was investigated to determine the effect of its microstructural parameters and densification on thermo-mechanical properties and thermal stress resistance to fracture initiation during a hot or cold mechanical and thermal shock testing. The different materials and microstructures were obtained by changing the parameters such as the type of the powder, additive, forming p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1989
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.38.1415