Evaluation of hydrogen-induced cracking in high-strength steel welded joints by acoustic emission technique
نویسندگان
چکیده
منابع مشابه
The Influence of Ultrasonic Impact Treatment on Fatigue Behaviour of Welded Joints in High-strength Steel
The unabated growth of the steel industry and progressively increasing operating loads on metal structures generate a need for a search for optimum engineering solutions to improve the loadcarrying capacity and reduce metal consumption. One way of resolving this problem is to utilise high-strength steels. It is common knowledge however that the improvement of the steel strength is accompanied b...
متن کاملOn the Use of Acoustic Emission and Digital Image Correlation for Welded Joints Damage Characterization
A series of tests have been conducted to investigate fatigue damage characterization in corroded welded steel plates using structural health monitoring (SHM) techniques. Acoustic Emission (AE) is a non-destructive testing (NDT) technique with potential applications for locating and monitoring fatigue cracks in service. In the present work, AE is implemented to characterize damage during crack e...
متن کاملsuppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولImproving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملThe Effect of Hydrogen Content and Welding Conditions on the Hydrogen Induced Cracking of the API X70 Steel Weld
In this study, first,diffusible hydrogen of cellulosic electrode E8010-P1 and low hydrogen electrode E8018-G was measured by mercury displacement method according to ISO3690. Then,the effect of preheating and post-heating on the sensitivity to hydrogen inducedcold cracking in welding of 18mm API5L X70 steel with these electrodes was investigated according to ISO17642-2. The results of visual in...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials & Design
سال: 2020
ISSN: 0264-1275
DOI: 10.1016/j.matdes.2020.108573