Evaluation of hydrogen absorption and desorption properties of Mg/Al based laminated thin films
نویسندگان
چکیده
منابع مشابه
architecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولPreparation and Hydrogen Absorption/Desorption of Nanoporous Palladium Thin Films
Nanoporous Pd (np-Pd) was prepared by co-sputtering Pd-Ni alloy films onto Si substrates, followed by chemical dealloying with sulfuric acid. X-ray diffractometry and chemical analysis were used to track the extent of dealloying. The np-Pd structure was changed from particle-like to sponge-like by diluting the sulfuric acid etchant. Using suitable precursor alloy composition and dealloying cond...
متن کاملHydrogen Absorption/Desorption Properties in the TiCrV Based Alloys
Three different Ti-based alloys with bcc structure and Laves phase were studied. The TiCr 1.1 V 0.9 , TiCr 1.1 V 0.45 Nb 0.45 and TiCr 1.1 V 0.9 + 4%Zr 7 Ni 10 alloys were melted in arc furnace under argon atmosphere. The hydrogen absorption capacity was measured by using aparatus type Sievert’s. Crystal structures, and the lattice parameters were determined by using X-ray diffraction, XRD. Mic...
متن کاملsome properties of fuzzy hilbert spaces and norm of operators
in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...
15 صفحه اولHydrogen Desorption/Absorption Properties of Li-Ca-N-H System
Hydrogen storage properties of two ball-milled composites of Ca(NH2)2+2LiH and CaH2+2LiNH2 were investigated as a series of searching studies of high performance hydrogen storage materials. About 4.5 mass% hydrogen is desorbed from about 100 °C and the thermal desorption profiles show a peak around 200 and 220 °C for the composites of CaH2+2LiNH2 and Ca(NH2)2+2LiH, respectively, under a helium ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the JSME (in Japanese)
سال: 2021
ISSN: 2187-9761
DOI: 10.1299/transjsme.21-00057