Evaluation of fracture resistance of stably growing crack by crack energy density (3rd report, Effect of sheet thickness on fracture resistance of ductile crack in thin plate)
نویسندگان
چکیده
منابع مشابه
Crack blunting, crack bridging and resistance-curve fracture mechanics in dentin: effect of hydration.
Few studies have focused on a description of the fracture toughness properties of dentin in terms of resistance-curve (R-curve) behavior, i.e., fracture resistance increasing with crack extension, particularly in light of the relevant toughening mechanisms involved. Accordingly, in the present study, fracture mechanics based experiments were conducted on elephant dentin in order to determine su...
متن کاملEffect of Constraint on Ductile Crack Growth and Ductile-Brittle Fracture Transition of a carbon Steel
Ductile-brittle fracture transition was investigated using compact tension (CT) specimens from -70 o C to 40 o C for a carbon steel. Large deformation finite element analysis has been carried out to simulate the stable crack growth in the compact tension (CT, a/W=0.6), three point-point bend (SE(B), a/W=0.1) and centre-cracked tension (M(T), a/W=0.5) specimens. Experimental crack tip opening di...
متن کاملExperimental Study of Sable Crack Growth in Thin Aluminium Sheet
Recent failure information from research teams in NASA Langley and others has shown that CTOA based fracture models calibrated on large C(T) and M(T) specimens can be transferred successfully to cracked aircraft fuselage structures for the assessment of their residual strength. A major difficulty that could limit the more extensive use of this failure parameter is its experimental measurement e...
متن کاملCrack Tip Constraint for Anisotropic Sheet Metal Plate Subjected to Mode-I Fracture
On the ground of manufacturing, sheet metal parts play a key role as they cover about half of the production processes. Sheet metals are commonly obtained from rolling and forming processes which causes misalignment of micro structure resulting obvious anisotropic characteristics and micro cracks. Presence of micro cracks poses serious attention, when stresses at the tip reach to the critical v...
متن کاملCrack Growth during Brittle Fracture
Title: Crack Growth During Brittle Fracture in Compression. Author: Bartlett W. Paulding, Jr. Submitted to the Department of Geology and Geophysics February 9, 1965 in partial fulfillment of the requirements for the degree of Doctor of Philosophy at the Massachusetts Institute of Technology. Photoelastic analysis of several two-crack arrays predicts that compressive fracture is initiated at cra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1986
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.52.1891