Evaluation of fatigue strength criteria for thick-walled nodular cast iron components from EN-GJS-400 under multiaxial load
نویسندگان
چکیده
منابع مشابه
A review on fatigue design of heavy section EN-GJS-400-18-LT ductile iron wind turbine castings
A comprehensive review of fatigue behavior and fatigue design of heavy section wind turbine castings made of ductile iron EN-GJS-400-18-LT is performed. Common metallurgical defects that are affecting fatigue behavior of this material were studied. Review of different researches on quantitative effect of chunky graphite and micro structure on fatigue behavior of EN-GJS-400-18-LT was perform...
متن کاملa review on fatigue design of heavy section en-gjs-400-18-lt ductile iron wind turbine castings
a comprehensive review of fatigue behavior and fatigue design of heavy section wind turbine castings made of ductile iron en-gjs-400-18-lt is performed. common metallurgical defects that are affecting fatigue behavior of this material were studied. review of different researches on quantitative effect of chunky graphite and micro structure on fatigue behavior of en-gjs-400-18-lt was performed. ...
متن کاملFatigue Behaviour of Synthetic Nodular Cast Irons
A. Vaško, L. Trško, R. Konečná, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic The paper shows the influence of charge composition on microstructure, fatigue properties and failure micromechanisms of nodular cast irons. The additive of metallurgical silicon carbide (SiC) in analysed specimens increases the content of ferrite in the matrix, decreases the size of...
متن کاملFailure Analysis of a Four Cylinder Diesel Engine Crankshaft Made From Nodular Cast Iron
The premature breakage in some four cylinder diesel engine crankshafts was reported. All crankshafts were failed from the same region. Failures had occurred in the first crankpin, the nearest crankpin to the flywheel. Dynamic analysis and finite element modelling were carried out to determine the state of stress in the crankshaft. FEM results revealed that the first crankpin fillet is the most ...
متن کاملPrediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria
In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2019
ISSN: 2261-236X
DOI: 10.1051/matecconf/201930016001