Evaluation of Dual-Cure Resin Cement Polymerization under Different Types and Thicknesses of Monolithic Zirconia
نویسندگان
چکیده
منابع مشابه
Curing efficiency of dual-cure resin cement under zirconia with two different light curing units
PURPOSE Adequate polymerization is a crucial factor in obtaining optimal physical properties and a satisfying clinical performance from composite resin materials. The aim of this study was to evaluate the polymerization efficiency of dual-cure resin cement cured with two different light curing units under zirconia structures having differing thicknesses. MATERIALS AND METHODS 4 zirconia discs...
متن کاملEvaluation of shear bond strength between dual cure resin cement and zirconia ceramic after thermocycling treatment
PURPOSE This study was performed to evaluate shear bond strength (SBS) between three dual-cured resin cements and silica coated zirconia, before and after thermocycling treatment. MATERIALS AND METHODS Sixty specimens were cut in 15 × 2.75 mm discs using zirconia. After air blasting of 50 µm alumina, samples were prepared by tribochemical silica coating with Rocatec™ plus. The specimens were ...
متن کاملLight curing of dual cure resin cement
266 This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/ by-nc/3.0) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
متن کاملLight transmittance of zirconia as a function of thickness and microhardness of resin cements under different thicknesses of zirconia
OBJECTIVE The objective of this study was to compare microhardness of resin cements under different thicknesses of zirconia and the light transmittance of zirconia as a function of thickness. STUDY DESIGN A total of 126 disc-shaped specimens (2 mm in height and 5 mm in diameter) were prepared from dual-cured resin cements (RelyX Unicem, Panavia F and Clearfil SA cement). Photoactivation was p...
متن کاملMicroleakage Evaluation of Class II Composite Resin Restorations with Different Thicknesses of Resin-Modified Glass Ionomer
Background and Aim: One of the weaknesses of Class II composite resin restorations is gingival microleakage which contributes to postoperative sensitivity and secondary caries. The aim was to evaluate the microleakage in Class II composite resin restorations with different thicknesses of resin-modified glass ionomer (RMGI). Materials and Methods: In this in-vitro study, standardized Class II s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: BioMed Research International
سال: 2019
ISSN: 2314-6133,2314-6141
DOI: 10.1155/2019/4567854