Side Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملFatigue Evaluation in Hot and Warm mix asphalts Based on Dissipated Energy
Warm mix asphalts (WMA), because of their low production and compact temperatures, may have different behaviors in long term. In the present work, the energy-based criteria along with the 50% reduction in initial stiffness (Nf50%) using four-point bending test under controlled-strain conditions of 1000 microstrain were applied to compare the prepared two warm mix and HMA samples. All these crit...
متن کاملLocation, location & size: defects close to surfaces dominate fatigue crack initiation
Metallic cast components inevitably contain defects such as shrinkage cavities which are inherent to the solidification process. Those defects are known to significantly alter the fatigue life of components. Yet very little is known, quantitatively, on the dangerosity of internal casting defects compared to surface ones. In this study, fatigue specimens containing controlled internal defects (s...
متن کاملThe role of grain boundaries on fatigue crack initiation – An energy approach
In this paper, we construct a model for prediction of fatigue crack initiation based on the material’s microstructure. In order to do so, the energy of a persistent slip band (PSB) is monitored and an energy balance approach is taken, in which cracks initiate and the material fails due to stress concentration from a PSB (with respect to dislocation motion). These PSBs are able to traverse low-a...
متن کاملEffects of Microstructure on Room Temperature Fatigue Crack Initiation and Short Crack Propagation in Udimet
An assessment of the effects of microstructure on room temperature fatigue crack initiation and short crack propagation in a Ni-base superalloy is presented. The assessment was carried out on microstructural variants of U720Li, including as-received U720Li, U720Li-LG (large grain variant) and U720Li-LP (large intragranular coherent γ′ variant). Fatigue tests were carried out at room temperature...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2015
ISSN: 0514-5163,1880-7488
DOI: 10.2472/jsms.64.668