Erratum:High-Pressure Sintering of the Amorphous TiAl Powder

Reactive Sintering of TiAl - Ti 5 Si 3 Lnsitu Composites

TiAl with between 0 and 20 volume percent (v%)Ti5Si3 was produced by reactive sintering of cofd pressed compacts of elemental Ti, Al and Si powder mixtures at 7OO0C for 15 minutes in vacuum. The results show that adding Si to Ti and A1 reduces the swelling associated with reactive sintering of TiAI, as composites containing more than 5 vYoTigSi3 densified during reactive sintering. However, com...

Nano Powder Direct Metal Sintering Systems Specification

Lubricant Pyrolysis During Sintering of Powder Metallurgy Compacts

The chemistry surrounding the pyrolysis of N,NЈ-ethylenebisstearimide (EBS) compacted with iron powder is described for the first time. Heat treatment is carried out in a 5 vol pct hydrogen atmosphere (balance nitrogen) over the 100 °C to 850 °C range. The exhaust from the furnace is monitored by Fourier transform infrared and dispersive ultraviolet absorption spectroscopy; condensable material...

Sintering Aids in Powder Metallurgy THE ROLE OF THE PLATINUM METALS IN THE ACTIVATED SINTERING OF REFRACTORY METALS

When a metallic powder is subjected to a suffkiently high pressure a certain amount of adhesion takes place between individual particles. If this compact i s then sintered the bond is improved by diflusion and intergranular grain growth. The earliest known platinum objects were fabricated by such a powder metallurgical process, and when European scientists first addressed the problem of manufac...

Sintering of Nd-Fe-B Magnets from Dy Coated Powder

High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...