Erosion Wear Properties of TiC-Al2O3 Composites
نویسندگان
چکیده
منابع مشابه
The Effect of TiC Additive with Al2O3-Y2O3 on the Microstructure and Mechanical Properties of SiC Matrix Composites
In this research, the SiC-matrix composite with different amounts of TiC (0, 2.5, 5, 7.5, and 10 wt%) supplemented with additives including 4.3 wt% Al2O3 and 5.7 wt% Y2O3 were utilized to initiate the required liquid phase. The sintering process was performed using pressureless sintering at 1900 °C for 1.5 hours under argon atmosphere. The compos...
متن کاملMechanical and Morphological Properties of Polypropylene/Nano α-Al2O3 Composites
A nanocomposite containing polypropylene (PP) and nano α-Al2O3 particles was prepared using a Haake internal mixer. Mechanical tests, such as tensile and flexural tests, showed that mechanical properties of the composite were enhanced by addition of nano α-Al2O3 particles and dispersant agent to the polymer. Tensile strength was approximately ∼ 16% higher than pure PP by increasing the nano α-A...
متن کاملErosion-corrosion and wear
The basic processes of wear, erosion and erosion-corrosion are reviewed. It is shown that oxide debris can accelerate wear when it is present as particulates, or protect and reduce friction when it is present as a glaze. Erosion-corrosion processes can be understood and organized in a series of regimes that represent a sequence of change in the relative intensities of erosive and corrosive proc...
متن کاملThree-body wear of different composites resins
Introduction: Low resistance of composite resins to abrasion is a primary concern in the application of these materials for posterior restorations which are prone to high occlusal loads. This study compared the wear resistance of three types of composites. Methods: In this laboratory experiment, five specimens of each of the three types of composites (z250, Heliomolar, Opallis) were prepared...
متن کاملMechanical and Wear Properties of Al-Nip Composites Produced by ARB Process
In this research, Al-Ni particle composite strips are formed by accumulative roll bonding (ARB) process using Al strips and Ni powder. The rule of ARB cycles and volume percentage (Vol%) of Ni powder on the microstructure, wear resistance and mechanical properties of the formed composites are investigated. According to the tensile test results, the yield stress and tensile strengths of the Al -...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2003
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.111.485