Erosion Resistance of Coatings Methods For Evaluating Erosion (Cavitation) Damage
نویسندگان
چکیده
منابع مشابه
Effect of Porosity on Cavitation Erosion Resistance of HVOF Processed Tungsten Carbide Coatings
The phenomenon of cavitation is widely experienced in both pumps and under-water components of hydro power plants. The mechanism of material damage during cavitation is mainly attributed to implosion of high velocity bubbles on to the surface giving raise to local increase in stresses in excess of 1.4 GPa. In addition, material wastage due to particle induced erosion is observed in hydro plants...
متن کاملComparison of cavitation erosion rate with liquid impingement erosion rate
Both cavitation erosion and liquid impingement erosion are phenomena that can cause pipe wall thinning in power plants. The Code for Power Generation Facilities, Rules on Pipe Wall Thinning Management, was published by the JSME (Japan Society of Mechanical Engineers) in 2005. The code says that cavitation erosion shall be prevented either in the design stage or by daily inspection. On the other...
متن کاملErosion and Foreign Object Damage of Thermal Barrier Coatings
Thermal barrier coating are perceived as an enabling technology to increase the performance of, improve efficiency within, and lower the emissions from, modern gas turbines. To fully utilise this capability one has to be able to accurately predict the life of these coatings under conditions relevant to gas turbine service. This paper addresses the failure of TBC systems as a result of erosion a...
متن کاملObservations of cavitation erosion pit formation.
Previous investigations showed that a single cavitation bubble collapse can cause more than one erosion pit (Philipp & Lauterborn [1]). But our preliminary study showed just the opposite - that in some cases a single cavitation pit can result from more than one cavitation event. The present study shows deeper investigation of this phenomenon. An investigation of the erosion effects of ultrasoni...
متن کاملTowards numerical prediction of cavitation erosion.
This paper is intended to provide a potential basis for a numerical prediction of cavitation erosion damage. The proposed method can be divided into two steps. The first step consists in determining the loading conditions due to cavitation bubble collapses. It is shown that individual pits observed on highly polished metallic samples exposed to cavitation for a relatively small time can be cons...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING DIGEST
سال: 1968
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1954.17.6-7_274