Ensemble magnetic behavior of interacting CoFe nanoparticles
Ferromagnetic nanoparticles in the 10–14 nm size range are examined for their size and interaction dependent magnetic properties. From X-ray magnetic circular dichroism the orbital-to-spin magnetic moment ratio is determined and found to decrease significantly with particle size. This is in accordance with previous complementary studies on smaller particles and highlights the difficulty of fitt...
متن کاملCoFe Layers Thickness and Annealing Effect on the Magnetic Behavior of the CoFe/Cu Multilayer Nanowires
CoFe/Cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. Nanowires with 30 nm diameter and the definite lengths were obtained. The effect of CoFe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. The layers thickness was controlled t...
متن کاملcofe layers thickness and annealing effect on the magnetic behavior of the cofe/cu multilayer nanowires
cofe/cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. nanowires with 30 nm diameter and the definite lengths were obtained. the effect of cofe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. the layers thickness was controlled t...
متن کاملMagnetic states of granular layered CoFe-Al2O3
The granular layered magnetic system Co80Fe20( )/Al2O3(3 nm), where the Co80Fe20 layers of nominal thickness form separate, almost spherical magnetic granules of typical diameter 2–3 nm between the Al2O3 spacers, was studied. We discuss measurements of the dc and ac magnetic susceptibility for 1 nm 1.3 nm at temperatures 10 K 300 K and ac frequencies 0.01 Hz 10 Hz, revealing a rich variety of m...
متن کاملSuperspin glass behavior of interacting ferromagnetic nanoparticles in discontinuous magnetic multilayers
Discontinuous magnetic multilayers [Co80Fe20(t)/Al2O3(3nm)]10 with t = 0.9 and 1.0nm are studied by SQUID magnetometry and ac susceptibility. Owing to dipolar interaction the superparamagnetic cluster systems undergo collective glass-like freezing upon cooling. While both samples exhibit very similar glass temperatures Tg ≈ 45 K and critical exponents zν ≈ 10 and γ ≈ 1.4 as obtained from the te...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frontiers in Physics
سال: 2015
ISSN: 2296-424X
DOI: 10.3389/fphy.2015.00052