Enhancement of photoluminescence from zinc oxide by aluminum nanoparticle surface plasmon
نویسندگان
چکیده
منابع مشابه
Gap-Plasmon Enhanced Gold Nanoparticle Photoluminescence
Gap-plasmon-enhanced gold nanoparticle photoluminescence is studied experimentally at the single-particle level. The photoluminescence spectra of gold nanoparticles on an Al2O3-coated gold film under both 532 and 633 nm excitation show a clear peak near the measured gap-plasmon resonance wavelength. Comparing the collected emission spectrum with that from a gold reference film under 633 nm exci...
متن کاملSynthesis of zinc oxide nanoparticle by zinc acetate precursor and study on its catalytic properties
ZnO nanoparticles have been prepared by a simple method in a short period of time. In this synthetic method, the sample was obtained using Zn(CH3COO)2·2H2O and a new template of hexamine salt. Their crystalline structure and morphology were studied by XRD and SEM. The optical properties of the sample were studied by UV–visible spectroscopy. The absorption spectr...
متن کاملPlasmon coupled nanoparticle arrays for fluorescence, photoluminescence and Raman scattering enhancement
We study the enhancement of the fluorescence an photoluminescence by large homogeneous arrays of plasmon coupled 5-8 nm Au and Ag nanoparticle separated by distances less than 10 nm. A red shift of the major “symmetric” plasmon mode near 780 nm, and additional “anti-symmetric” plasmon mode centered near 310 nm evidence the plasmon coupling in Au particle arrays. The systems were found to be eff...
متن کاملSynthesis of zinc oxide nanoparticle by zinc acetate precursor and study on its catalytic properties
ZnO nanoparticles have been prepared by a simple method in a short period of time. In this synthetic method, the sample was obtained using Zn(CH3COO)2·2H2O and a new template of hexamine salt. Their crystalline structure and morphology were studied by XRD and SEM. The optical properties of the sample were studied by UV–visible spectroscopy. The absorption spectr...
متن کاملEnhanced ultraviolet sensitivity of zinc oxide nanoparticle photoconductors by surface passivation
0925-3467/$ see front matter 2010 Elsevier B.V. A doi:10.1016/j.optmat.2010.09.020 ⇑ Corresponding author. Tel.: +1 518 276 2164; fax E-mail address: [email protected] (S. Sawyer). Zinc oxide nanoparticles were created by a top-down wet-chemical etching process and then coated with polyvinyl-alcohol (PVA), exhibiting sizes ranging from 10 to 120 nm with an average size approximately 80 nm. T...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Physica Sinica
سال: 2019
ISSN: 1000-3290
DOI: 10.7498/aps.68.20190062