Enhancement Mechanical Properties of B4C Ceramics with the Core-Shell Structure Powders
نویسندگان
چکیده
In order to improve the mechanical properties of B4C ceramics, B4C@TiB2 composite powders with core-shell structure are prepared by molten salt method using and Ti as raw materials. And ceramics were from spark plasma sintering (SPS). The results show that exhibit intact structure. improves mass transfer during sintering. When molar ratio B4C/Ti is 2/1, relative density, Vickers hardness, fracture toughness flexural strength BT1/2 sample 94.2%, 26.9 GPa, 5.34 MPa·m1/2 570 MPa, respectively, which best comprehensive properties.
منابع مشابه
modification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
determination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولCore–shell grain structures and ferroelectric properties of Na0.5K0.5NbO3–LiTaO3–BiScO3 piezoelectric ceramics
Legislation arising from health and environmental concerns has intensified research into finding suitable alternatives to lead-based piezoceramics. Recently, solid solutions based on sodium potassium niobate (K,Na)NbO3 (KNN) have become one of the globally-important lead-free counterparts, due to their favourable dielectric and piezoelectric properties. This data article provides information on...
متن کاملCore-shell Grain Structures and Dielectric Properties of Na0.5K0.5NbO3-LiTaO3-BiScO3 Piezoelectric Ceramics
The origins of distinctive compositional dependence of relative permittivity, 計r, in the Pb-free piezoelectric system (1-x)Na0.5K0.5NbO3-xLiTaO3, x≤ 10 mol% modified with BiScO3 have been revealed using transmission electron microscopy with energy dispersive X-ray analysis (TEM-EDX). As the LiTaO3 content increased the Curie peak at ~370°C in 計r –T plots became more diffuse, and at x= 5 mol% an...
متن کاملGain optimization of the optical waveguide based on the quantum box core/shell structure
In order to implement an integrated optical quantum circuit, designing waveguides based on the quantum box is of prime importance. To do this we have investigated optical waveguide both with and without optical pumping. The rate of absorption and emission using an array of AlGaAs/GaAs quantum box core/shell structure in the optical waveguide with various pumping intensities has computed. By con...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in transdisciplinary engineering
سال: 2022
ISSN: ['2352-751X', '2352-7528']
DOI: https://doi.org/10.3233/atde220433