Enhanced field emission properties from well-aligned zinc oxide nanoneedles grown on the Au∕Ti∕n-Si substrate

Enhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates

Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...

Field emission properties of individual zinc oxide nanowire field emitter

The authors report the field emission FE properties of individual ZnO nanowire field emitters. ZnO nanowire field emitter directly grown on a Pt tip showed a much better field emission current delivery than the attached nanowire emitters due to better contact properties. The emission current and field emission microscopy pattern of the ZnO nanowire are strongly influenced by adsorbates. After t...

Core-shell InGaAs/GaAs quantum well nanoneedles grown on silicon with silicon-transparent emission.

In(x)Ga(1-x)As wurtzite nanoneedles are grown without catalysts on silicon substrates with x ranging from zero to 0.15 using low-temperature metalorganic chemical vapor deposition. The nanoneedles assume a 6 degrees - 9 degrees tapered shape, have sharp 2-5 nm tips, are 4 microm in length and 600 nm wide at the base. The micro-photoluminescence peaks exhibit redshifts corresponding to their inc...

Enhanced electron field emission properties of high aspect ratio silicon nanowire-zinc oxide core-shell arrays.

The enhanced electron field emission (EFE) properties of high aspect ratio, vertically aligned SiNW-ZnO core-shell arrays are presented. These core-shell arrays are prepared by a thin, controlled, highly crystalline and conformal coating of zinc oxide as shell using the plasma assisted-atomic layer deposition (PA-ALD) route on vertically aligned silicon nanowire arrays core. The core-shell nano...

Piezoelectric power generation from zinc oxide nanowires grown on paper substrate