Empirical Viscosity Modeling for SiO2 and Al2O3 Nanofluids using the Response Surface Method
نویسندگان
چکیده
منابع مشابه
Measuring and Modeling Viscosity of CaO-Al2O3-SiO2(-K2O) Melt
The effect of K2O on viscosity in CaO-SiO2-Al2O3 melt has been measured by a rotating spindle viscometer. It is indicated from the experimental results that viscosity first increases then decreases with the increasing content of K2O; the maximum viscosity occurs in the field of K2O/ Al2O3 > 1. After gradually adding K2O, the transformation of bridging oxygen (from being bonded with Al ion charg...
متن کاملpreparation and characterization of new co-fe and fe-mn nano catalysts using resol phenolic resin and response surface methodology study for fischer-tropsch synthesis
کاتالیزورهای co-fe-resol/sio2و fe-mn-resol/sio2 با استفاده از روش ساده و ارزان قیمت همرسوبی تهیه شدند. از رزین پلیمری resol در فرآیند تهیه کاتالیزور استفاده شد.
Viscosity affected by nanoparticle aggregation in Al2O3-water nanofluids
An investigation on viscosity was conducted 2 weeks after the Al2O3-water nanofluids having dispersants were prepared at the volume concentration of 1-5%. The shear stress was observed with a non-Newtonian behavior. On further ultrasonic agitation treatment, the nanofluids resumed as a Newtonian fluids. The relative viscosity increases as the volume concentrations increases. At 5% volume concen...
متن کاملIntrinsic viscosity of SiO2, Al2O3 and TiO2 aqueous suspensions.
The viscosity of dilute suspensions of several metal oxides (SiO2, Al2O3 and TiO2) was measured at different pH values. The intrinsic viscosity, [eta], was derived from the concentration dependence of the viscosity. This magnitude was pH-dependent. A correlation with the shape of the kinetic unity has been proposed.
متن کاملSynthesis of Nanoscale CaO-Al2O3-SiO2-H2O and Na2O-Al2O3-SiO2-H2O Using the Hydrothermal Method and Their Characterization
C-A-S-H (CaO-Al₂O₃-SiO₂-H₂O) and N-A-S-H (Na₂O-Al₂O₃-SiO₂-H₂O) have a wide range of chemical compositions and structures and are difficult to separate from alkali-activated materials. Therefore, it is difficult to analyze their microscopic properties directly. This paper reports research on the synthesis of C-A-S-H and N-A-S-H particles with an average particle size smaller than 300 nm by apply...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Advanced Research in Fluid Mechanics and Thermal Sciences
سال: 2020
ISSN: 2289-7879
DOI: 10.37934/arfmts.75.3.6372