Elektrodepolama ile Üretilen Co, Ni ve CoNi Alaşımlı İnce Filmlerin Yapısal ve Manyetik Özelliklerinin İncelenmesi

The production of nanoparticles as thin film coating performed with electrodeposition method is easier and cheaper than other methods. Because, can be controlled the change ingredients in bath composition. In this study, Co, Ni, CoNi alloy films were fabricated through composition that consists cobalt sulphate (CoSO4.7H2O), nickel (NiSO4.6H2O), (II) chloride (NiCl2 6H2O) boric acid (H3BO3). Crystal structure (XRD), morphological (SEM), elemental (ICP) magnetic properties (VSM) investigated. Chemical (CV) was examined well. Magnetization measurements by applying fields between + 75000 Oe -75000 then hysteresis loops obtained. showed ferromagnetic material properties. Coercivity (Hc), permanent magnetization (Mr), saturation (Ms) values these alloys significantly affected amount cobalt, magneto crystal anisotropy grain size. It understood some materials having hard soft controlling