Electropolishing Behavior of 8xxx Al Alloy in Perchloric Acid and Ethanol Solution
نویسندگان
چکیده
Abstract The electropolishing characteristic curves of rolled 8079 Al alloy in perchloric acid and ethanol solution from -25 °C to 25 are obtained. optimal conditions the with investigated by optical microscope. result shows that lower temperature is, longer time range voltage wider. Furthermore, calibration rate phase after is higher than 97% Electron Back-Scatter Diffraction. effect both cast 8011 (cast rolled) verified.
منابع مشابه
Spectral Transmittance Characteristics of Holmium Oxide in Perchloric Acid Solution
Accepted: November 28, 1984 The work describes the methods and procedures used to determine the wavelengths of minimum transmittance of holmium oxide in perchloric acid solution. Measurements of spectral transmittance of the solutions were made by means of a high precision spectrophotometer over the wavelength range 200 nm to 680 nm. The wavelength scale accuracy of this instrument was verified...
متن کاملEFFECTS OF Al-5TI-1B MASTER ALLOY AND HEAT TREATMENT ON THE MICROSTRUCTURE AND DRY SLIDING WEAR BEHAVIOR OF AN Al-12Zn-3Mg-2.5Cu ALLOY
In this study the effect of Al–5Ti–1B grain refiner on the structural characteristics and wear properties of Al–12Zn–3Mg–2.5Cu alloy was investigated. The optimum amount for Ti containing grain refiners was selected as 2 wt.%. T6 heat treatment, (i.e. heating at 460 °C for 1 h before water quenching to room temperature and then aging at 120 °C for 24 h) was applied for all specimens before wear...
متن کاملEffect of Deformation-Induced Defects on the Microstructure and Pitting Corrosion Behavior of Al-Ag Alloy
In this study, a wide range of combined ageing treatments and cold work deformations in the Al 4.2 wt% Ag alloy matrix were proposed, aiming to investigate the effect of defects such as precipitates (Ag2Al plates) and dislocations on the mechanical and electrochemical behavior of Al–4.2 wt% Ag alloys. Further reductions of thickness from 10 to 60%, decreases the mean size of Ag2...
متن کاملAging behavior in Cu–Al–Be shape memory alloy
This article reports positron annihilation spectroscopy and calorimetric measurements of the aging behavior in a Cu–Al–Be shape memory alloy. An excess of single vacancies is retained in the alloy as a result of a quench. All vacancies in excess disappear after long aging time, and a migration energy EM51.060.1 eV for this process has been found to be larger than in other Cu-based shape memory ...
متن کاملThe Electrochemical Behavior of Al Alloys in NaCl Solution in the Presence of Pyrazole Derivative
This paper studies the corrosion inhibition of Al-Mg alloy system in 0.5 mol/dm3 NaCl solution in the presence of pyrazole derivative using potentiodynamic polarization and linear polarization method. The inhibition efficiency as a function of concentration and temperature was investigated. From the polarization curves, it can be concluded that the pyrazole derivative be...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of physics
سال: 2023
ISSN: ['0022-3700', '1747-3721', '0368-3508', '1747-3713']
DOI: https://doi.org/10.1088/1742-6596/2529/1/012021