Electroplating of Co-W and Co-Mo Alloys from Na2WO4 Ionic Melts

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

a r t i c l e i n f o Zn–Ni, Zn–Co and Zn–Ni–Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency ...

Behavior of disordered Co-Pd, Co-Ag, and Co-Mo alloys in multilayer interfaces

Composition, Morphology, and Topography of Galvanic Coatings Fe-Co-W and Fe-Co-Mo

Ternary coatings Fe-Co-W with an iron content of 40-55 at.%, cobalt 39-44 at.%, and tungsten 4-12 at.% and Fe-Co-Mo with an iron content of 40-55 at.%, cobalt 39-44 at.%, and tungsten 4-12 at.% were obtained by galvanostatic and pulse electrolysis on the mild steel substrate from iron(III) citrate-based electrolyte. The influence of electrolysis mode and parameters on composition of deposited a...

CORROSION RESISTANCE OF Co-Cr-Mo ALLOY USED IN DENTISTRY ODPORNOŚĆ KOROZYJNA STOPU Co-Cr-Mo WYKORZYSTYWANEGO W STOMATOLOGII

The presented paper studies the effect of the casting technology on the corrosion resistance of Co-Cr-Mo alloy. The investigations were conducted on a commercial alloy with the brand name ARGELOY N.P SPECIAL (Co-Cr-Mo) produced by Argen as well as the same alloy melted and cast by the lost wax casting method performed by a dental technician. The corrosion behavior of the dental alloys in an art...

Comparison of Dental Prostheses Cast and Sintered by SLM from Co-Cr-Mo-W Alloy

The article presents the results of a comparative analysis of the metal substructure for dental prosthesis made from a Co-Cr-Mo-W alloy by two techniques, i.e. precision investment casting and selective laser melting (SLM). It was found that the roughness of the raw surface of the SLM sinter is higher than the roughness of the cast surface, which is compensated by the process of blast cleaning ...