Electroless Plating of Ni-Co-Fe-P Alloy for Soft Magnetic Thin Films.

Soft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films

Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 ◦C are saturation magnetization 9.13 × 105 A/m, coercivity 79...

Effect of Cobalt Concentration on Structural and Magnetic Properties of Co-Fe Thin Films

Co-Fe films were electrodeposited on Cu substrate from electrolytes with different Co concentration  levels. X-ray diffraction (XRD) was used  to  investigate  the  films  crystal  structures. The  results  indicate that  if  the  Co  concentration  is  less  that  the  Fe  concentration,  the cubic  structure  appears  in  the  films, while  the  hexagonal  structure dominates when  the C...

Electroless Nickel Plating on Magnesium Alloy

he inherent lightness and good strength-to-weight ratio of T magnesium has focused attention on increasing applications in aerospace and allied fields. Its density is two thirds that of aluminum-a conventional structure material for aerospace. Magnesium has one drawback: It is prone to atmospheric corrosion. Further, because of its high chemical affinity for aqueous solutions, it is categorized...

Combinatorial study of Fe-Co-V hard magnetic thin films

Thin film libraries of Fe-Co-V were fabricated by combinatorial sputtering to study magnetic and structural properties over wide ranges of composition and thickness by high-throughput methods: synchrotron X-ray diffraction, magnetometry, composition, and thickness were measured across the Fe-Co-V libraries. In-plane magnetic hysteresis loops were shown to have a coercive field of 23.9 kA m-1 (3...

Diffraction studies on Ni-Co and Ni-Cr alloy thin films