Electroless Ni-B Plating in the Tartrate-complexed Ni Solution.
نویسندگان
چکیده
منابع مشابه
Electroless Ni–P composite coatings
This review outlines the development of electroless Ni–P composite coatings. It highlights the method of formation, mechanism of particle incorporation, factors influencing particle incorporation, effect of particle incorporation on the structure, hardness, friction, wear and abrasion resistance, corrosion resistance, high temperature oxidation resistance of electroless Ni–P composite coatings ...
متن کاملMechanisms and solutions to the brittle solder joint in electroless Ni plating
Brittle solder joints in Electroless Ni electroless Pd immersion Au (ENEPIG) surface finishes are one of the key re liability issues in electronics assembly. Previous characterization of the reflow process has indicated that interfa cial voids formed after solder reflow are responsible for the decreases in solder joint strength. However, the mechanisms behind the formation of these voids in t...
متن کاملRoughness Optimization of Electroless Ni-B Coatings Using Taguchi Method
In this paper, the authors present an experimental study of roughness characteristics of electroless Ni-B coatings and optimization of the coating process parameters based on L27 Taguchi orthogonal design. Three coating process parameters are considered viz. bath temperature, reducing agent concentration, and nickel source concentration. It is observed that concentration of reducing agent toget...
متن کاملNi-B Coating Production on Magnesium Alloy by Electroless Deposition
The use of magnesium alloys is limited due to their susceptibility to corrosion although they have many attractive physical and mechanical properties. To increase mechanical and corrosion properties of these alloys, many deposition method and coating types are used. Electroless Ni–B coatings have received considerable interest recently due to its unique properties such as cost-effectiveness, th...
متن کاملThe Root Cause of Black Pad Failure of Solder Joints with Electroless Ni/Immersion Gold Plating
This paper reports on a study of the reaction of solder with the electrolessnickel with immersion gold (ENIG) plating system, and the resulting interfacial structures. A focused-ion beam (FIB) was used to polish the cross sections to reveal details of the microstructure of the ENIGplated pad with and without soldering. High-speed pull testing of solder joints was performed to expose the pad sur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 2002
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.53.65