ELECTRODEPOSITION OF CO-DOPED HYDROXYAPATITE COATING ON 316L STAINLESS STEEL
نویسندگان
چکیده
منابع مشابه
Alumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملCoating of strontium substituted hydroxyapatite on surface treated surgical grade stainless steel by electrodeposition for biomedical applications
Surgical grade stainless steel (316L SS) is one of the widely used implant material in orthopedic surgeries. But often the release of metal ions is evidenced from the implants and subsequently a second surgery is required to remove the implant material. One way to control the release of metal ions is to coat the implant material with a biocompatible material like hydroxyapatite (HAp). Strontium...
متن کاملCharacterization of CrN/TiN PVD Coatings on 316L Stainless Steel
In order to further enhance tribological properties 316 Low carbon stainless steel (L SS) used on mechanical parts. CrN/TiN with DC magnetron sputtering sources was carried out on PVD 316 L SS. The micro structure of the CrN/TiN coatings were investigated by Scanning electron microscope (SEM), X-ray Diffraction (XRD) and tribology properties were investigated on a Pin on Disc friction and wear ...
متن کاملBiomaterial Studies on AISI 316L Stainless Steel after Magnetoelectropolishing
The polarisation characteristics of the electropolishing process in a magnetic field (MEP – magnetoelectropolishing), in comparison with those obtained under standard/conventional process (EP) conditions, have been obtained. The occurrence of an EP plateau has been observed in view of the optimization of MEP process. Up-to-date stainless steel surface studies always indicated some amount of fre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Vietnam Journal of Science and Technology
سال: 2018
ISSN: 2525-2518,2525-2518
DOI: 10.15625/2525-2518/56/1/10030