Electrodeposition of amorphous Ni-Fe-P alloys.
نویسندگان
چکیده
منابع مشابه
Ternary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کاملSonochemical preparation of nanosized amorphous Fe-Ni alloys
Nanosized amorphous alloy powders of Fe20Ni80 , Fe40Ni60 , and Fe60Ni40 were prepared by sonochemical decomposition of solutions of volatile organic precursors, Fe~CO!5 and Ni~CO!4 in decalin, under an argon pressure of 100 to 150 kPa at 273 K. Magnetic susceptibility of Fe40Ni60 and Fe60Ni40 indicates blocking temperatures of 35 K and a magnetic particle size of about 6 nm. Thermogravimetric m...
متن کاملELECTRODEPOSITION OF Ni-Fe ALLOYS FROM SULFATE, SULFATE-CHLORIDE AND CHLORIDE BATHS
In an attempt to control the film composition, factors affecting the composition of Ni-Fe alloy deposits and their crystal structure have been analyzed as a function of bath composition, cathode current density, bath pH, temperature and an addition of citric acid. antimony electrode revealed that the deposition potential of Fe coincides with the potential where the abrupt increase of pH was obs...
متن کاملA Novel Electrodeposition Process for Plating Zn-Ni-Cd Alloys
Zn-Ni-Cd alloy was electrodeposited from an alkaline electrolytic bath under potentiostatic conditions. Bath analyses using a pH concentration diagram reveal that addition of a complexing agent is essential to maintain the bath stability. Introduction of a low concentration of CdSO4 reduces the anomalous nature of the Zn-Ni deposit. Deposits obtained from the electrolytic bath which contains 60...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1989
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.40.431