Electrodeposited Porous Mn1.5Co1.5O4/Ni Composite Electrodes for High-Voltage Asymmetric Supercapacitors
نویسندگان
چکیده
منابع مشابه
Electrodeposited Porous Mn1.5Co1.5O4/Ni Composite Electrodes for High-Voltage Asymmetric Supercapacitors
Mesoporous Mn1.5Co1.5O₄ (MCO) spinel films were prepared directly on a conductive nickel (Ni) foam substrate via electrodeposition and an annealing treatment as supercapacitor electrodes. The electrodeposition time markedly influenced the surface morphological, textural, and supercapacitive properties of MCO/Ni electrodes. The (MCO/Ni)-15 min electrode (electrodeposition time: 15 min) exhibited...
متن کاملComposite Electrodes for Electrochemical Supercapacitors
Manganese dioxide nanofibers with length ranged from 0.1 to 1 μm and a diameter of about 4-6 nm were prepared by a chemical precipitation method. Composite electrodes for electrochemical supercapacitors were fabricated by impregnation of the manganese dioxide nanofibers and multiwalled carbon nanotubes (MWCNT) into porous Ni plaque current collectors. Obtained composite electrodes, containing 8...
متن کاملHierarchical nanostructures of polypyrrole@MnO2 composite electrodes for high performance solid-state asymmetric supercapacitors.
A solid-state high performance flexible asymmetric supercapacitor (ASC) was fabricated. Its anode is based on organic-inorganic materials, where polypyrrole (PPy) is uniformly wrapped on MnO2 nanoflowers grown on carbon cloth (CC), and its cathode is made of activated carbon (AC) on CC. The ASC has an areal capacitance of 1.41 F cm(-2) and an energy density of 0.63 mW h cm(-2) at a power densit...
متن کاملNitrogenated porous carbon electrodes for supercapacitors
Nitrogenated porous carbon materials, made by coating the pore surface with nitrogen functional groups from the pyrolysis of hexamine, were characterized and tested for supercapacitor applications. From X-ray photoelectron spectroscopy, the nitrogen content of the nitrogenated carbon sample was found to be 14 wt%. Electrochemical properties from potentiostatic and galvanostatic measurements, an...
متن کاملSeries asymmetric supercapacitors based on free-standing inner-connection electrodes for high energy density and high output voltage.
Asymmetric supercapacitors (ASCs) based on free-standing membranes with high energy density and high output voltage are reported. MnO(2) nanowire/carbon nanotube (CNT) composites and MoO(3) nanobelt/CNT composites are selected as the anode and the cathode materials of the devices, respectively. The ASC has a high volumetric capacitance of 50.2 F cm(-3) at a scan rate of 2 mV s(-1) and a high op...