Electrochemical Study on the Pitting and Crevice Corrosion of 18Cr-8Ni Stainless Steel

IMPROVING PITTING CORROSION OF 304 STAINLESS STEEL BY ELECTROPOLISHING TECHNIQUE

Several surface modification techniques such as ion implantation, surface laser melting, have been employed to improve pitting corrosion resistance of stainless steel. Electropolishing is a technique in which the surface roughness is eliminated through a selective electrochemical dissolution. The effect of electropolishing on pitting corrosion of 304 stainless steel (SS) was investigated employ...

Stainless steel pitting and early-stage stress corrosion cracking under ultra-low elastic load

The Inhibition Effect of Polyethylenimine (PEI) on Pitting Corrosion of 304 Austenitic Stainless Steel in 3.5% NaCl Solution

One of the problems in the case of stainless steels is their low corrosion resistance against pitting corrosion in chloride containing environments, thereby leading to severe damage to industries. In this research, the pitting corrosion of 304 austenitic stainless steel was studied in 3.5% NaCl solution at room temperature (25˚C) by performing electrochemical measurements (containing cyclic pol...

Electrochemical deprotonation of phosphate on stainless steel

Voltammetric experiments performed in phosphate buffer at constant pH 8.0 on platinum and stainless steel revealed clear reduction currents, which were correlated to the concentrations of phosphate. On the basis of the reactions proposed previously, a model was elaborated, assuming that both H2PO4 and HPO4 2 underwent cathodic deprotonation, and including the acid–base equilibriums. A kinetic m...

DETERIORATION OF PITTING CORROSION OF 316 STAINLESS STEEL BY SENSITIZATION HEAT TREATMENT

In this research pitting Corrosion of a sensitized 316 stainless steel was investigated employing potentiodynamic, potentiostatic techniques. Sensitization process was carried out on as-received alloy by submitting the specimen in electric furnace set at 650°Cfor five hours and then the specimen was quenched 25°C water. Potentiodynamic polarization of as received and sensitized specimens in 1M ...