Electrochemical Noise of SCC Inhibition of a Supermartensitic Stainless Steel in Sour Solution

نویسندگان

چکیده

In this work, the inhibition effect of a non-ionic gemini surfactant, named bis(2-((2-palmitoamidoethyl)amino)ethyl)1H-imidazole4,5-dicarboxylate, on stress corrosion cracking (SCC) behavior supermartensitic stainless steel (SMSS) was studied in sour environment. The slow strain rate tests (SSRT) results and fractographic analysis revealed that inhibitor able to inhibit SCC process using concentration above than 5ppm. At concentrations 0 5 ppm, showed brittle fracture with susceptibility SCC, whereas at 25 100 ductile, practically immune SCC. EN measurements transients associated pits microcracks, which were confirmed by SEM examination. shot noise theory indicated localized dominant SMSS susceptible

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Electrochemical Characterization of a Martensitic Stainless Steel

This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 ...

متن کامل

Mechanism of SCC on SUS310S Stainless Steel

The author have developed a new SCC test method that enables the super Kelvin force microscope (SKFM) and the Kelvin force microscope (KFM) observations. By using this test device, the crack tip deformation and surface potential distribution were observed on SUS310S stainless steel by SKFM and KFM. At the same time, the distribution of hydrogen was examined by the Ag decoration method with the ...

متن کامل

Electrochemical Characterization of a Martensitic Stainless Steel

This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 ...

متن کامل

ELECTROCHEMICAL BEHAVIOUR OF AISI 304 STAINLESS STEEL IN SULFURIC SOLUTION: EFFECTS OF ACID CONCENTRATION

The effects of H2SO4 concentration on the electrochemical behaviour of passive films formed on AISI 304 stainless steel were investigated using by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Potentiodynamic polarization indicated that the corrosion potentials were found to shift towards negative direction with an increase in solution co...

متن کامل

Prediction of Time to Failure in SCC of 304 Stainless Steel in Aqueous Chloride Solution Using Neural Network

Prediction of SCC risk of austenitic stainless steels in aqueous chloride solution and estimation of the time to failure as a result of SCC form important and complicated topics for study. Despite the many studies reported in the literature, a formulation or a reliable method for the prediction of time to failure as a result of SCC is yet to be developed. This paper is an &#10effort to investig...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: ECS transactions

سال: 2023

ISSN: ['2151-2051', '1938-5862', '1938-6737']

DOI: https://doi.org/10.1149/11001.0029ecst