Electrochemical Corrosion in Bars of AISI 304 Embedded in Concrete Immersed in Marine-Sulfated Environment
نویسندگان
چکیده
The electrochemical behavior of the corrosion resistance AISI 304 embedded in concrete manufactured as indicated by ACI 211.1 method was evaluated. specimens were exposed for more than 150 days to highly aggressive marine-sulfated environment, solution with a concentration 5% NaCl and Na2SO4. technique Resistance Linear Polarization (Rp) used determine rate (Icorr) monitoring potential (Ecorr). Ecorr Icorr results indicate high level 1018 steel, on contrary, behaviour steel according values Icorr, up 10 times higher when an environment chlorides sulfates.
منابع مشابه
Corrosion of Reinforcing Bars in Concrete
The causes and mechanisms of corrosion of reinforcing bars in concrete are described in terms of the practical issues as well as the electrochemistry. The parameters affecting corrosion are (i) the ingress of aggressive species, such as chlorides, which break down the protective film on the reinforcing bar and (ii) the amount of those species necessary to do so. The former is largely controlled...
متن کاملCorrosion in Concrete Structures with Permanent Deformation in Marine Environment
Concrete is usually highly alkaline (pH around 12), thus protecting reinforcement against corrosion. The occurrence of oxides is favored when the medium pH surrounding the bar is in values near to 9 or lower. Aggressive substances for reinforcements generally enter concrete through its pore structure, and cracks tend to decrease pH, stimulating corrosion process. There are several causes for cr...
متن کاملDeterioration of Concrete in Ambient Marine Environment (RESEARCH NOTE)
Structural concrete exposed to marine environment deserves special attention as the diffused sea salts chemically react with harden cement matrix and forms various expansive/leachable compounds leading to loss of material, strength, cracking, spalling etc. This study cover the effect of sea water on the specimens cast from two grades of concrete exposed to simulated marine environment over a ye...
متن کاملInfluence of Nano-Silica and Silica Fume in the Steel Corrosion Embedded in Concrete
Corrosion of steel is one of the most important potential dangers and threats in concrete structures. Corrosion of steel embedded in reinforced concrete plays a key role in reducing the strength and durability of reinforced concrete. Several studies have proposed that alternative approaches to enhancing the performance of reinforced concrete and its resistance to corrosion. In this study, the r...
متن کاملMonitoring Corrosion of Steel Bars in Reinforced Concrete Structures
Corrosion of steel bars embedded in reinforced concrete (RC) structures reduces the service life and durability of structures causing early failure of structure, which costs significantly for inspection and maintenance of deteriorating structures. Hence, monitoring of reinforcement corrosion is of significant importance for preventing premature failure of structures. This paper attempts to pres...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: European Journal of Engineering and Technology Research
سال: 2023
ISSN: ['2736-576X']
DOI: https://doi.org/10.24018/ejeng.2023.8.1.2942