Electrocaloric response in lanthanum-modified lead zirconate titanate ceramics

Large Electrocaloric Effect in Relaxor Ferroelectric and Antiferroelectric Lanthanum Doped Lead Zirconate Titanate Ceramics

Both relaxor ferroelectric and antiferroelectric materials can individually demonstrate large electrocaloric effects (ECE). However, in order to further enhance the ECE it is crucial to find a material system, which can exhibit simultaneously both relaxor ferroelectric and antiferroelectric properties, or easily convert from one into another in terms of the compositional tailoring. Here we repo...

A. Response of Lead Zirconate Titanate Ceramics to Temperature Fluctuations

It has been found that some shapes of lead zirconate titanate (PZT) ceramics respond to rapid temperature fluctuations when mounted in a particular geometrical configuration. This effect is presumably caused by thermal stresses in the crystal which produce a voltage difference across the silvered surfaces. These units were originally constructed to serve as pressure transducers in a lowpressure...

Measurement of Flexoelectric Effect in Lead Zirconate Titanate Ceramics*

Lead zirconate titanate (PZT) ceramics is usually used as a piezoelectric material. However it has characteristics of not only piezoelectricity but also flexoelectricity. Piezoelectricity is a phenomenon that electric polarization is induced by strain, and flexoelectricity is the one that the polarization is induced by strain gradient. In this study, flexoelectricity in poled soft PZT ceramics ...

Piezoelectricity in Lead-Zirconate-Titanate Ceramics – Extrinsic and Intrinsic Contributions

Crack tip 90° domain switching in tetragonal lanthanum-modified lead zirconate titanate under an electric field

Lanthanum-modified lead zirconate titanate ferroelectric ceramics (Pb0.96La0.04)(Zr0.40Ti0.60)0.99O3 were synthesized by the conventional powder processing technique. X-ray diffraction experiments revealed that the samples belong to the tetragonal phase with a 4 b 4 0.4055 nm, c 4 0.4109 nm, and c/a 4 1.013. After being poled, the samples were indented with a 5-kg Vickers indenter, and lateral ...