Electrical and optical properties of MoO3-V2O5 mixed oxide films
نویسندگان
چکیده
منابع مشابه
Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولstructural, electrical and optical properties of molybdenum oxide thin films prepared by post-annealing of mo thin films
molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using dc magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°c) with flow oxygen at 200 sccm (standard cubic centimeter per minute). the crystallographic structure of the films was obtained by means of x-ray diffraction (xrd) analysis. an atomic force micr...
متن کاملStudy of optical absorption and optical band gap determination of thin amorphous TeO2-V2O5-MoO3 blown films
The optical absorption coefficient of amorphous 40TeO2-(60-x) V2O5-xMoO3 thin films was determined in a spectral range 190-1100 nm at room temperature. The fundamental optical absorption edge was sharp. The optical gap generally increases as the proportion of MoO3 in the mixed films increases. The width of the tail of the localized states in the band gap was determined for different composition...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 1996
ISSN: 0250-4707,0973-7669
DOI: 10.1007/bf02745155