Elastic properties and indentation cracking behavior of Na2O-TiO2-SiO2 glasses

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Interaction between Deformation and Crack Initiation under Vickers Indentation in Na2O–TiO2–SiO2 Glasses

An observed minimum in the critical crack initiation load at Poisson’s ratio (ν) of 0.21–0.22 in Na2O–TiO2–SiO2 glasses was investigated. Vickers indentation was used to examine hardness and average cracking length, fracture toughness was measured through the single-edge pre-cracked beam method, and volumes of densification and shear flow around indents were measured using atomic force microsco...

متن کامل

Magnetic properties of praseodymium ions in Na2O–Pr2O3–SiO2 glasses

Sodium praseodymium silicate glasses of nominal composition 0.3Na2O xPr2O3 (0.7 x)SiO2, where 0pxp0:10; have been studied by magnetisation and X-ray photoelectron spectroscopy (XPS). The magnetisation data fail to collapse to a single curve in the M versus H=T representation for all values of x and the spread increases with x; indicating an increase in the magnetic exchange interaction. The M v...

متن کامل

Structural Investigation of Na2O–B2O3–SiO2 Glasses Doped with NdF3

Abstract—Sodium borosilicate glasses doped with different content of NdF3 mol % have been prepared by rapid quenching method. Ultrasonic velocities (both longitudinal and shear) measurements have been carried out at room temperature and at ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature, softening temperature and Poisson's ratio have been obtained as a function of NdF3 modifier...

متن کامل

X-ray photoelectron spectroscopy of CeO2–Na2O–SiO2 glasses

A series of (CeO2)x–(Na2O)0.3–(SiO2)(0.7−x) glasses, where 0.025≤ x≤ 0.075, have been synthesized and investigated by mean of X-ray photoelectron spectroscopy (XPS). The Ce 3d spin-orbit doublet was curve fitted in order to quantify the proportions of each cerium oxidation state in these glasses. It was found that Ce ions are predominantly in the Ce(III) state in glasses with compositions x≤ 0....

متن کامل

COMPOSITION DEPENDENCE OF SPECTROSCOPIC PROPERTIES AND TRANSPARENCY OF SiO2-TiO2-Na2O GLASS IN 200-1100 nm

Abstract: Glassy samples with xTiO2 .3SiO2 .Na2O composition that (8≤x≤40) (molar) were casted in refractory steel molds after melting at air as parallel palates. After polishing and getting to desire thickness, UV-VIS spectrometry in 200 -1100 nm was measured on samples. Glass density was measured by a sensitive micro balance and was found that by increasing titanium dioxide of glasses, glass ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of Non-Crystalline Solids

سال: 2015

ISSN: 0022-3093

DOI: 10.1016/j.jnoncrysol.2015.09.011