Effects of Zr Additive on Microstructure, Mechanical Properties, and Fractography of Al-Si Alloy
نویسندگان
چکیده
منابع مشابه
Effects of Zr Additive on Microstructure, Mechanical Properties, and Fractography of Al-Si Alloy
The effects of Zr additive on the microstructure, mechanical properties, and fracture behavior of Al-Si alloy were systematically investigated. The additive of Zr obviously reduced the size of Si particles and changed its morphology. Grain size refinement was promoted by the reaction between Al and Zr forming Al3Zr and ZrSi2 compounds. Compared to a Zr-free alloy, the additive enhanced the tens...
متن کاملEffect OF SI and AL on the Microstructure, Mechanical Properties and Machinability of 65CU-35ZN Brass
Relations between the microstructure, mechanical properties and machinability of as-cast 65Cu-35Zn brass with various amounts of Al from 0 to 4.72 and Si from 0 to 3.62 wt% were investigated. Both Si and Al initially enhanced the UTS and toughness of the brass samples, which led to improvement in machinability due to a reduction in the main cutting force. A duplex brass with random oriented α p...
متن کاملEffect of Al–5Ti–C Master Alloy on the Microstructure and Mechanical Properties of Hypereutectic Al–20%Si Alloy
Al-5Ti-C master alloy was prepared and used to modify hypereutectic Al-20%Si alloy. The microstructure evolution and mechanical properties of hypereutectic Al-20%Si alloy with Al-5Ti-C master alloy additions (0, 0.4, 0.6, 1.0, 1.6 and 2.0 wt%) were investigated. The results show that, Al-5Ti-C master alloy (0.6 wt%, 10 min) can significantly refine both eutectic and primary Si of hypereutectic ...
متن کاملMicrostructure and mechanical properties of a precipitation-strengthened Al-Zr-Sc-Er-Si alloy with a very small Sc content
The precipitation hardening behavior of an Al-0.08Zr-0.014Sc-0.008Er-0.10Si (at.%) alloy was investigated utilizing microhardness, electrical conductivity, atom-probe tomography (APT), and compressive creepmeasurements. This new composition, with a Sc:Zr atomic ratio of less than 1:5 represents a significant reduction of the alloy's cost when compared to the more usual Al-0.06Sc-0.02Zr based al...
متن کاملInfluence of Rolling Temperature on Microstructure and Mechanical Properties of Cryorolled Al-Mg-Si Alloy
An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ∼0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respe...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2018
ISSN: 2075-4701
DOI: 10.3390/met8020124