Effects of Silicon Content and Austempering Conditions on Impact Strength in Austempered Spheroidal Graphite Cast Steel.
نویسندگان
چکیده
منابع مشابه
the effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)
cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...
the impact of e-readiness on ec success in public sector in iran the impact of e-readiness on ec success in public sector in iran
acknowledge the importance of e-commerce to their countries and to survival of their businesses and in creating and encouraging an atmosphere for the wide adoption and success of e-commerce in the long term. the investment for implementing e-commerce in the public sector is one of the areas which is focused in government‘s action plan for cross-disciplinary it development and e-readiness in go...
On the Effect of Pouring Temperature on Spheroidal Graphite Cast Iron Solidification
This work is focused on the effect of pouring temperature on the thermal-microstructural response of an eutectic spheroidal graphite cast iron (SGCI). To this end, experiments as well as numerical simulations were carried out. Solidification tests in a wedge-like part were cast at two different pouring temperatures. Five specific locations exhibiting distinct cooling rates along the sample were...
متن کاملthe washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests
در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است
15 صفحه اولEffects of Homogenization Conditions and Hot Rolling Parameters on Grain Refinement of an As-Cast 301 Stainless Steel
In this work, effects of homogenization time of 3 to 13 h at 1200 °C on the grain refinement of as-cast AISI 301 stainless steel after different hot rolling conditions were investigated. The results showed that the minimum grain size of 16±7 mm was achieved when homogenization took place at 1200 °C for 9 h followed by hot rolling at temperature range of 1000–1200 °C with strain of 0.8 and stra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1994
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.60.2357