Effects of rejuvenation heat treatment on microstructure and creep property of a Ni-based single crystal superalloy

Evaluating the Effect of Ta/W Ratio on Microstructure and Stress Rupture Properties of Ni-Based Single Crystal Superalloy PWA1483

In this study, the effect of Ta/W ratio on the microstructure and stress rupture properties of Ni-based single crystal (SX) superalloy PWA1483 was investigated. For this purpose, single crystal (SX) superalloys with different Ta/W ratios (0.75, 1.0, 1.32 and 1.5 in wt.%) were fabricated. The alloys were directionally solidified by Bridgman method under the same solidification condition at withd...

Lattice strain evolution and load partitioning during creep of a Ni-based superalloy single crystal with rafted microstructure

In-situ neutron diffraction measurements were performed on monocrystalline samples of the Ni-based superalloy CMSX-4 during N-type g0 raft formation under the tensile creep conditions of 1150 C/ 100 MPa, and subsequently on a rafted sample under the low temperature/high stress creep conditions of 715 C/825 MPa. During 1150 C/100 MPa creep, the g0 volume fraction decreased from ~70% to ~50%, the...

the effect of heat treatment on the microstructure of cast ni-based in100 superalloy

the purpose of this study was to investigate the effect of heat treatment including solution treatment and aging on the microstructure of cast nickel-based in100 superalloy including size, volume fraction and morphology of primary γ' and different kinds of carbides. for this purpose, different solution heat treatment cycles and a constant aging cycle were implemented on cast ingot samples and t...

Creep and Stress Relaxation Anisotropy of a Single-Crystal Superalloy

Determination of solution temperature in an ex-service Ni-based turbine blade

It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover their microstructures. The first and main step of rejuvenation process is the determination of appropriate solution condition in ...