Effects of Prestrain on Fatigue Behaviour in Type 316 Stainless Steel
نویسندگان
چکیده
منابع مشابه
The Unified Creep-Fatigue Equation for Stainless Steel 316
Background—The creep-fatigue properties of stainless steel 316 are of interest because of the wide use of this material in demanding service environments, such as the nuclear industry. Need—A number of models exist to describe creep-fatigue behaviours, but they are limited by the need to obtain specialized coefficients from a large number of experiments, which are time-consuming and expensive. ...
متن کاملFatigue and fracture of a 316 stainless steel metal matrix composite reinforced with 25% titanium diboride
Fatigue and fracture mechanisms have been studied in a steel-based metal matrix composite (MMC), comprising a 316L austenitic matrix reinforced with 25 wt% particulate titanium diboride (TiB2). The fracture toughness was determined in the as-HIPped condition as being slightly below 30 MPa√m. Fatigue crack growth rates have been determined, and corrected for the effects of crack closure. The fra...
متن کاملThe adhesion of hot-filament CVD diamond films on AISI type 316 austenitic stainless steel
Steel ball indentation and scratch adhesion testing of hot filament chemical vapour deposited diamond films onto AISI type 316 austenitic stainless steel substrates using two different interlayer systems, namely chromium nitride and borided steel, have been investigated. In order to compare the adhesion of these films with that of a well-known and strongly adherent system, detailed adhesion tes...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملFatigue behavior of Austenitic Type 316L Stainless Steel
The aim of this work is to determine the fatigue life of 316L stainless steel. The mechanisms of fatigue of 316L stainless steels were investigated and discussed. The fatigue tests were carried out at constant-amplitude cyclic loading with load ratio R=0.1. Scanning Electron Microscope (SEM) is then used to examine the fracture surface. The results show that the fatigue limit of 316L stainless ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 2007
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.73.796