Effects of photo-assisted electrodeposited on CuInSe2 thin films
نویسندگان
چکیده
منابع مشابه
Effects of photo-assisted electrodeposited on CuInSe2 thin films
Photo-assisted one-step electrodeposition has been applied to help in forming smooth and dense CuInSe2 films. The difference in surface morphology and crystalline quality between CuInSe2 films with various photo-assistance has been investigated. In the photo-assisted electrodeposition process, the many kinds of lamps providing maximum light intensity at about 380 to 620 nm were used as light so...
متن کاملElectrodeposited CuInSe2 thin film junctions
We have investigated thin films and junctions based on copper indium diselenide (CIS) which have been grown by electrochemical deposition. CIS is a leading candidate for use in polycrystalline thin film photovoltaic solar cells. Electrodeposition is a cost-effective method for producing thin-film CIS. We have produced both p and n type CIS thin films from the same aqueous solution by simply var...
متن کاملSynthesis of CuInSe2 thin films from electrodeposited Cu11In9 precursors by two-step annealing
In this study, copper indium selenide (CIS) films were synthesized from electrodeposited Cu-In-Se precursors by two-step annealing. The agglomeration phenomenon of the electrodeposited In layer usually occurred on the Cu surface. A thermal process was adopted to turn Cu-In precursors into uniform Cu11In9 binary compounds. After deposition of the Se layer, annealing was employed to form chalcopy...
متن کاملONE STEP ELECTRODEPOSITION OF CuInSe2 THIN FILMS
Formation of CuInSe2 (CIS) thin films from aqueous solution containing citrate as complexing agent is reported. The surface morphology and the composition of the deposited films are characterized by scanning electron microscopy (SEM). The texture of the deposits and their compositions are analyzed by X-ray diffraction and transmission electron microscopy (TEM). Annealing of the films at 350°C i...
متن کاملProperties of Electrodeposited WO3 Thin Films
Galvanostatic electrodeposition was used to produce transparent and amorphous WO3 films that showed color changes from clear to blue in response to the applied potential of ±1.0 V. The 61% in transmittance variation was measured at wavelength of 633 nm. The roughness of 16.7 nm was obtained by atomic force microscopy (AFM). The scanning electron microscopy (SEM) evidenced homogeneous morphology...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2014
ISSN: 1556-276X
DOI: 10.1186/1556-276x-9-660