Effects of Heat Treatment on Corrosion Attack of Stainless Steel (SEC 15) Weld Parts
نویسندگان
چکیده
منابع مشابه
Effect of ageing heat treatment on corrosion behaviorof 17-4 PH stainless steel in 3.5% NaCl
The 17-4PH alloy is a martensitic stainless steel with 3–5 wt% Cu, strengthened by the precipitation hardening. Due to excellent mechanical properties, corrosion resistance and ease of heat treatment, this alloy has unique applications in nuclear power plants and marine constructions. In this paper, the influence of ageing heat treatment, solution annealing followed by ageing at 480, 550 and 62...
متن کاملDETERIORATION OF PITTING CORROSION OF 316 STAINLESS STEEL BY SENSITIZATION HEAT TREATMENT
In this research pitting Corrosion of a sensitized 316 stainless steel was investigated employing potentiodynamic, potentiostatic techniques. Sensitization process was carried out on as-received alloy by submitting the specimen in electric furnace set at 650°Cfor five hours and then the specimen was quenched 25°C water. Potentiodynamic polarization of as received and sensitized specimens in 1M ...
متن کاملEffect of heat treatment on stainless steel orthodontic wires.
This study evaluated the effect of heat treatment on CrNi stainless steel orthodontic archwires. Half of forty archwires of each thickness - 0.014" (0.35 mm), 0.016" (0.40 mm), 0.018" (0.45 mm) and 0.020" (0.50 mm) (totalling 160 archwires) - were subjected to heat treatment while the remainder were not. All of the archwires had their individual thickness measured in the anterior and posterior ...
متن کاملeffect of ageing heat treatment on corrosion behaviorof 17-4 ph stainless steel in 3.5% nacl
the 17-4ph alloy is a martensitic stainless steel with 3–5 wt% cu, strengthened by the precipitation hardening. due to excellent mechanical properties, corrosion resistance and ease of heat treatment, this alloy has unique applications in nuclear power plants and marine constructions. in this paper, the influence of ageing heat treatment, solution annealing followed by ageing at 480, 550 and 62...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1955
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.24.7_241