Effect of WC content on microstructure, hardness, and wear properties of plasma cladded Fe-Cr-C-WC coating
نویسندگان
چکیده
منابع مشابه
Effect of WC Concentration on Abrasive Wear Properties of the Thermally Sprayed WC -Ni Coatings
In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstr...
متن کاملThe Effect of sintering temperature on microstructure and hardness of milled WC- 20 wt.% equiatomic (Fe,Co) cemented carbides
In this study, WC–20 wt.% equiatomic (Fe,Co) powder mixture was milled in a planetary ball mill. The effects of different milling time (15 min, 5h, 10h, and 25 h) and sintering temperatures on the microstructure and mechanical properties of this equi-Fe substituted cermet were investigated. The structural evolution and the crystallite size changes of the powders during milling were monitored by...
متن کاملEffect of Chromium Content on Microstructure and Wear Resistance of Fe-Cr-C Hard facing Layers
Layers of Fe-Cr-C Hard facing material containing various amounts of chromium were deposited on mild steel base metal. Optical Microscope (OM), Scanning Electron Microscope (SCM) and X-ray diffraction (XRD) were used to investigate the effect of chromium content of micro structural characteristics of Fe-Cr-C hard facing layers. The M7C3 carbide refinement mechanism exists on base metal. The exp...
متن کاملEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملEffect of Wet and Dry Conditions on Wear Behavior of Amorphous Coating of Fe-Cr-Mo-Nb-C-B
Recently, wear resistant properties of metallic glasses has attracted a lot of interest. Because the surface of metallic glasses are prone to phase transformation, finding the effects of test condition on structure and wear behavior of metallic glasses is important. In this research, by using an automated electrospark deposition (ESD), a layer of Fe51Cr18Mo7B16C4Nb4 was deposited on AISI 316l s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2021
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ac0b79