Effect of Sputtering Gas Pressure on Mechanical Properties of TiN Coating Deposited by DC Magnetron Sputtering
نویسندگان
چکیده
منابع مشابه
The tribological properties of Cu-Ni3Al-MoS2 composite coating deposited by magnetron sputtering
In industrial applications, most materials are exposed to wear and friction because multiple conditions are used. However, the tribological properties of these materials can be improved with different techniques. One such technique that improves the frictional property of a surface is the use of self-lubricating coatings. In this study, multicomponent coatings of nominal composition Cu-Ni3Al-Mo...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کاملDeposited Indium Tin Oxide (ito) Thin Films by Dc- Magnetron Sputtering on Polyethylene Terephthalate Substrate (pet)
M.K.M. ALI , K. IBRAHIM , OSAMA S HAMAD , M.H. EISA , M.G. FARAJ , and F. AZHARI 1 School of Physics, University Sains Malaysia, Penang 11800, Malaysia Department of Physics, College of Science, Sudan University of Science and Technology, Khartoum 11113, Sudan School of Electrical and Electronic Engineering, University Sains Malaysia, Penang 11800, Malaysia E-mail: [email protected], kamarul@...
متن کاملAlNXOY THIN FILMS DEPOSITED BY DC REACTIVE MAGNETRON SPUTTERING
AlNxOy thin films were produced by DC reactive magnetron sputtering, using an atmosphere of argon and a reactive gas mixture of nitrogen and oxygen, for a wide range of partial pressures of reactive gas. During the deposition, the discharge current was kept constant and the discharge parameters were monitored. The deposition rate, chemical composition, morphology, structure and electrical resis...
متن کاملSuperhard NbB2-x thin films deposited by dc magnetron sputtering
We have deposited weakly textured substoichiometric NbB2-x thin films by magnetron sputtering from a NbB2 target. The films exhibit superhardness (42 ± 4 GPa), previously only observed in overstoichiometric TiB2 thin films, and explained by a self-organized nanostructuring, where thin TiB2 columnar grains hinder nucleation and slip of dislocations and a B-rich tissue phase between the grains pr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 2004
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.70.636