Effect of Solidification Variables on the Tensile Property of 2.8 wt% C–26 wt% Cr White Iron

The present study aimed to investigate the increasing solidification rate during directional developed from in situ composites of M7C3/austenite eutectic, with a small portion dendrites, and partial equiaxed structures. M7C3 fibre aligned along solidified direction composites; however, its orientation shape became irregular among dendrites. In composite structure has higher tensile strength than or material. Crack initiation occurred because could not accommodate deformation matrix under stress. fracture was caused by both crack initiations at randomly oriented particles, propagation matrix.