Effect of Si Content in Steel on Formation of Fe-Zn Intermetallic Compound Layer at Pure Zn Melt/Steel Interface

نویسندگان
چکیده

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

REACTION KINETICS OF THE FORMATION OF INTERMETALLIC Fe – Zn DURING HOT - DIP GALVANIZING OF STEEL

P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic This review article mainly describes the composition of intermetallic Fe Zn, i.e. zeta (ζ), delta (δ1k + δ1p), gamma1 (Γ1) and gamma (Γ) on galvanized steel during low temperature galvanization (t ~ 450 °C). It gives detail...

متن کامل

the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests

در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است

15 صفحه اول

Electron Diffraction Study on Fe–Zn intermetallic Phase of a Galvannealed IF Steel Sheet

In order to investigate the structure of Fe–Zn phase in a commercial galvannealed IF steel sheet, the electron diffraction and composition of phase in a commercial galvannealed IF steel sheet were studied by transmission electron microscope (TEM) and X-ray energy dispersive spectroscopy (EDX). The cross-sectional TEM specimen was prepared using focused ion beam (FIB) technique which was also in...

متن کامل

Control of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel

The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...

متن کامل

Tribological Behaviour of Fe-Al Intermetallic Compound Coated Carbon Tool Steel

The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. The microstructure...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Tetsu-to-Hagane

سال: 2014

ISSN: 0021-1575,1883-2954

DOI: 10.2355/tetsutohagane.100.390