Effect of Potassium Sulfate on the Portland Cement Pastes Setting Behavior
نویسندگان
چکیده
The article deals with the effect of potassium sulfates on setting behavior cement pastes. It has been established that main elements (Ca, Si, Al) are distributed in composition clinker minerals, while K and S atoms concentrated locally pores formation arcanite. is shown interaction K2SO4 CaSO42H2O followed by syngenite K2Ca(SO4)2H2O causes destructive phenomena
منابع مشابه
The Effect of Sulfate on the Electrical Properties of Cement Pastes
Exposure conditions significantly affect the resistance of cement to sulfate attack. This article investigates the effect of sulfate on electrical conductivity of ordinary Portland cement (OPC). Cement paste specimens were prepared according to water/cement (W/C) ratio equal 0.25 either free of sodium sulfate or its addition with concentrations of 5000ppm, 10000ppm and 15000ppm by weight. This ...
متن کاملEffect of additives on the compressive strength and setting time of a Portland cement.
Improvements in strength and setting time of Portland cements (PC) are needed to enhance their performance as endodontic and load bearing materials. This study sought to enhance the compressive strength and setting time of a PC by adding one of the following additives: 20% and 30% poly-methylmethacrylate (PMMA), 20% and 30% irregular and spherical amalgam alloys, and 10% CaCl(2). The control co...
متن کاملEffect of nanosilica additions on Belite cement pastes held in sulfate solutions
Fly Ash Belite cement (FABC) pastes with and without nanosilica additions have been prepared and maintained in sulfate solutions (Na2SO4 0.5 M) for 180 days. The mechanical performance and the changes in microstructure have been monitored at 28, 90 and 180 days by compressive strength, X-ray diffraction (XRD) and Si MAS NMR measurements. We have found that, unexpectedly, and contrary to what ha...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملCompressive strength of Portland cement pastes and mortars containing Cu-Zn nano-ferrite
This study is concerned with the synthesizing of Cu-Zn nano-ferrite particles in the laboratory applying simple techniques. The morphology of the synthesized nano-particles was analyzed using Transmission Electron Microscopy (TEM), and the minerals were identified using X-ray diffraction (XRD). The nano material was used to replace 1- 4 percent by weight of Portland cement in cement pastes and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chemistry and Chemical Technology
سال: 2023
ISSN: ['1996-4196']
DOI: https://doi.org/10.23939/chcht17.01.170