Effect of ion irradiation in austenitic stainless steel.
نویسندگان
چکیده
منابع مشابه
Structural transformations in austenitic stainless steel induced by deuterium implantation: irradiation at 100 K
Deuterium thermal desorption spectra were investigated on the samples of austenitic stainless steel 18Cr10NiTi preimplanted at 100 K with deuterium ions in the dose range from 3 × 10(15) to 5 × 10(18) D/cm(2). The kinetics of structural transformation development in the implantation steel layer was traced from deuterium thermodesorption spectra as a function of implanted deuterium concentration...
متن کاملStructural Transformations in Austenitic Stainless Steel Induced by Deuterium Implantation: Irradiation at 295 K.
Deuterium thermal desorption spectra were investigated on the samples of austenitic steel 18Cr10NiTi pre-implanted at 295 K with deuterium ions in the dose range from 8 × 10(14) to 2.7 × 10(18) D/cm(2). The kinetics of structural transformation development in the steel layer was traced from deuterium thermodesorption spectra as a function of deuterium concentration. Three characteristic regions...
متن کاملExperimental Quantification of Phase Transformation in Austenitic Stainless Steel
This conference paper briefly discusses different techniques for measuring the evolution of the martensite content in cold-rolled stainless steel 301LN sheets under mechanical loading. Three methods are employed to measure the martensite content: (1) micrography, (2) bulk magnetic induction, and (3) local magnetic permeability measurements. The first two methods require the extraction of sample...
متن کاملUltrasonic Characterization of Austenitic Stainless Steel in Thermal Variations
This work focuses on the ultrasonic characterization and hardness of Austenitic stainless steel in thermal variation. The sample which was heat treated at 1050 o C has the highest hardness value and plays a dominant role in dispersion of carbides. Shear wave velocity and hardness show similar trend in variation with temperature. The effect of volume expansion would be to decrease the elastic co...
متن کاملImprovement in the Corrosion Resistance of Austenitic Stainless Steel 316L by Ion Implantation*
In the present work, austenitic stainless steel 316L (SS316L) samples were implanted with Ni and Ni-Cr. A nickel-rich layer about 100 nm in thickness and a Ni-Cr enriched layer about 60 nm thick are formed on the surface of SS316L. The effects of ion implantation on the corrosion performance of SS316L are investigated in a 0.5 M H2SO4 with 2 ppm HF solution at 80°C by open circuit potential (OC...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1991
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.38.419