Effect of grain size on compression behavior of magnesium processed by Equal Channel Angular Pressing
نویسندگان
چکیده
منابع مشابه
Size effect in equal channel angular pressing (ECAP) process
The influence of the sample size (diameter while keeping the length constant) in equal channel angular pressing (ECAP) of pure aluminum is examined using finite element method (FEM) and experiment. Different sized aluminum rods were processed via ECAP and the effect of sample size on the strain homogeneity, process load, and the ratio of the friction to the total force were evaluated. The resul...
متن کاملCharacteristics of Cavitation in a Superplastic Magnesium Az31 Alloy Processed by Equal- Channel Angular Pressing
Experiments were conducted on a magnesium AZ31 alloy to evaluate the role of cavitation in high temperature superplasticity. Samples were processed by equal-channel angular pressing (ECAP) and then pulled to failure in tension at a temperature of 623K. Similar tests were also conducted on the as-received alloy. The results show the development of significant internal cavitation in this alloy wh...
متن کاملAchieving superplastic properties in a ZK10 magnesium alloy processed by equal-channel angular pressing
Equal-channel angular pressing provides an opportunity for refining the grain structure and introducing superplastic properties in magnesium alloys. This report describes the use of this processing technique with a ZK10 (Mg–1.0 wt.% Zn–0.26 wt.% Zr) alloy. The grain structure was successfully refined from ∼12.9 to ∼5.2 m after 4 passes and superplastic elongations were observed when testing at ...
متن کاملRe-strengthening in AA6063 Alloy During Equal Channel Angular Pressing
Equal channel angular pressing (ECAP) is carried out using two different configurations for the exit channel of the ECAP die, i.e., relieved and choked, with angles of 0.2 °. It is found that using a die with relieved exit channel, the sample was extruded for 6 passes with no surface cracks and an average cell size of 727 nm and a fraction of high angle grain boundaries of 54 % were achieved. M...
متن کاملHot and Cold Tensile Behavior of Al 6061 Produced by Equal Channel Angular Pressing and Subsequent Cold Rolling
The full annealing AA6061 aluminum alloy was subjected to severe plastic deformationvia the combination of equal channel angular pressing (ECAP) and cold rolling (CR) in order torefine its microstructure and to improve its mechanical properties. According to the results of hotand cold tensile tests, the combination of ECAP and CR significantly affected the final strengthand ductility of studied...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research and Technology
سال: 2013
ISSN: 2238-7854
DOI: 10.1016/j.jmrt.2013.03.009